Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Highlight
- Fast dry enables quick topcoat application
- Thin film resulting in low orange peel
- High solvency yields excellent adhesion over various substrates and treatments
- Product Info
Epoxy Primer Overview
Epox-Zen™ Epoxy Primers are a substantial upgrade from conventional alkyd primers and provide durable protection over ferrous and non-ferrous metals, specific FRPs and composites. Epox-Zen™ Epoxy Primers should be top coated with epoxy or polyurethane finishes to achieve the ultimate in protection and durability.
Epoxy Primary Characteristics
Epox-Zen™ Epoxy Primers are engineered to offer the finest corrosion protection, chemical resistance, adhesion and topcoat hold-out. Epox-Zen™ Epoxy Primers also dry quickly, enabling quick topcoat application.
Applications & Uses
- Applications
- Compatible Substrates & Surfaces
- Best For
- Boating
- Plastics
- Fiberglass
- Industries where quick recoat properties are desired
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Optimum Dry Film Thickness | 1.0 | mils | - |
Gloss (60°) | max. 10 | - | - |
Mix Ratio (Part A:Part B) | 4:1 | ||
VOC | 5.0 | lbs/gal | - |
ls HAPs Free Formula | Yes | - | - |
30 Minute Induction Time Needed | Yes | - | - |
Pot Life (Before 50% Increase in Viscosity) | 8.0 | hours | - |
Wet Film Sag Resistance | 4.0 | mils | - |
Air Dry to Touch | 30.0 | minutes | - |
Air Dry to Handle (Hard Dry) | 90.0 | minutes | - |
Air Dry Full Cure | 2.0 | Weeks | - |
Force Cure - Ambient Flash Time Before Baking | 10.0 | minutes | - |
Force Cure - Recommended Cure Time (180°) | 10.0 | minutes | - |
Minimum Dry Time Before Product can be Sanded (After Bake) | 16.0 | hours | - |
Minimum Dry Time Before Topcoat Application (After Bake) | 10.0 | minutes | - |
Maximum Dry Time Before Topcoat Application | 48.0 | hours | - |
Corrosion Resistance | Great | - | - |