Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Product Features
- Halogen free 3rd party independent tested.
- Non-sagging gaps filled to 0.372 inch.
- Superior impact and peel strength.
- Little or no surface preparation.
- Rapid room temperature cure.
- 100% reactive.
- Excellent environmental resistance.
Applications & Uses
- Markets
- Cure Method
- Handling and Application
Mixing
It is highly recommended that either meter mix equipment or cartridges with static mix nozzles be used to properly ratio and dispense the adhesive. Heat buildup during and after mixing is normal.
ApplyingBonding surfaces should be clean, dry, and free of contamination. Extensive surface preparation is not required for Fusionbond® 372 and good bonds can be formed on most substrates after a solvent wipe. To assure maximum bond strength, surfaces must be mated within the adhesive's open time. Use enough material to completely fill the joint when parts are clamped.
CuringParts should remain undisturbed during the interval between the adhesive’s open time and fixture time. After the fixture time is achieved the material has reached handling strength. Cure temperatures below room temperature (70ºF to 75ºF) may slow the fixturing time. Temperatures above room temperature will shorten the open time and the fixturing time.
Clean UpIt is important to clean up excess adhesive from the work area and application equipment before it cures. Use Hernon® EF® Cleaner 62 for removing uncured adhesive. Fusionbond® 372 is flammable. Keep containers tightly closed after use. Keep away from heat, sparks, and open flames.
Properties
- Typical Properties (Uncured)
Property Part A Part B Chemical Type Methacrylate Methacrylate Appearance Blue White Specific gravity 0.97 0.94 Viscosity at 25°C, CP 30,000 to 50,000 30,000 to 50,000
Mix ratio (by weight) 1 1 - Typical Curing Performance
Property Value Working time, minutes 15 to 20 Fixture time*, G/B steel, minutes 10 to 15 *Fixture time is defined as the time to develop a shear strength of 0.1 N/mm².
- Typical Cured Performance
Shear Strength, ASTM D1002 Gritblasted lap-shear specimens
Substrate Cure at 22ºC Value, psi Aluminum 24 Hours ≥ 2000 Steel 24 Hours ≥ 2000 Steel 24 Hours + 25 min @ 400ºF (204ºC) ≥ 3500 Steel 72 Hours ≥ 2000 Impact Strength, ASTM D6110 Gritblasted lap-shear specimens
Substrate Cure at 22ºC Value Steel 24 Hours >30 Joules Steel 24 hours + 25 min @ 400 ºF (204 ºC) ≥ 25 Joules Aluminum 24 Hours >24 Joules T-peel Strength, ASTM D1876 Gritblasted lap-shear specimens
Substrate Cure Time at 22ºC Value Aluminum 24 hours ≥ 20 PIW - Typical Environmental Resistance
Cured for 24hrs @ 22ºC Steel lap-shear specimens (grit blasted)
Cold & Hot Strength
Shear Strength, ASTM D1002
Test Condition Value, psi At 22 ºC ≥ 2000 At -40ºC, cold strength ≥ 3000 At 95ºC, hot strength ≥ 4000 Impact Strength, ASTM D6110
Test Condition Value, Joules At 22 ºC >30 At -40ºC, cold strength 10 - 20 At 95ºC, hot strength 35 - 45
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Bondable Substrates
- ABS.
- Acrylics (PMMA).
- Phenolics.
- Aluminum.
- Polycarbonate and blends.
- Brass.
- Polyurethanes ¹.
- Ceramics.
- PVC & Vinyls.
- Copper.
- Stainless steel.
- Fiberglass.
- Steel.
(¹ May need special treatment)
- General Information
This product is not recommended for use in pure oxygen and/or oxygen rich systems and should not be selected as a sealant for strong oxidizing materials. For safe handling information on this product, consult the Safety Data Sheet (SDS).
Storage & Handling
- Storage
Fusionbond® 372 should be stored in a cool, dry location in unopened containers at a temperature between 45ºF and 85ºFunless otherwise labeled. Shelf life can be extended by refrigeration at 45ºF to 55ºF (7ºC to 13ºC). To prevent contamination of unused material, do not return any material to its original container.