Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Features
- Permanent anti-static property HIPS
- After water washing to the injected parts , it still show the original anti-static property.
- Almost the same mechanical property as per the compounded process
- Heat stable ability
- Suitable for IC relative product and also the injecting parts in which sensitive to be out of order in static environment
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application Method
- Suitable for normal injection machine
- Injection Tempture recommend as between 190 ℃ ~200 ℃
- Various pigment for colorize are available
- Without and further procedure and additive .
Properties
- Color
- Appearance
- Pale yellow Pellet
- Typical Properties
Value | Units | Test Method / Conditions | |
Bending | 383 | kgf/cm2 | — |
Bending Elastic | 19228 | — | — |
Elongation | 19.3 | % | — |
Impact | 4.2 | kgf.cm/cm | — |
Melt Flow Rate (200 ℃ ,5kg) | 8.89 | g/10min | — |
Softening Point | 91.4 +/- 10 | ℃ | — |
Specific Gravity | 1.057 | — | — |
Tensile Strength | 200 | kgf/cm2 | — |
Thermal degradation Temperature | 78.5 | — | — |
Technical Details & Test Data
- Drying of HSINSOU ET-HIPS
HSINSOU ET-HIPS has some hygroscopic property but is packed in bags under moisture proof conditions ; no drying is necessary when used just after unsealing .
If HSINSOU ET-ABS kept open for a long time (about 72 hours) , drying is necessary before using .
Recommend Drying Temperature around 105℃ ~ 110℃ , Drying time is 1 ~ 2 hours.
- Property Test
Test report of ET-HIPS as following , It show the superior character of Anti-static after water washing .
Item \ Product HSINSOU ET-HIPS Surface Resistivity Before water washing 109 ~10 11 After 5 times water washing 109 ~10 11 Tensile Strength kgf/cm2 330 Elongation % 53.7