Knowde Enhanced TDS
Identification & Functionality
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Properties
Depending on the curing agent used, the formulated coatings yield the following performances:
- Favorable melt viscosity
- Ready pigment incorruption
- Good storage stability
- Good flow
- High gloss
- Very good mechanical properties
Applications & Uses
- Applications
- Cure Method
- Coating Type
- Application
Araldite GT 7004 is highly suitable for the formulation of powder coatings when cured with accelerated phenolic resins, dicyandiamide derivatives, novolacs, various acid anhydrides or saturated acid polyester resins.
Properties
- Appearance
- Clear, No Contamination
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Color (Gardner) | max. 1 | — | ASTM D-1544 |
| Epoxy Value | 1.33 – 1.40 | eq/Kg | ASTM D-1652 |
| Weight per Epoxide | 714 - 752 | g/eq | ASTM D-1652 |
| Viscosity at 25°C (77°F) | 500 - 600 | mPa.s | ISO 12058-1 |
| Softening Point (Mettler) | 95 - 101 | °C | ASTM D-3461 |
| Density at 25°C | 1.19 | g/cm3 | ISO 8130 |
| Flash Point | min. 200 | °C | ISO 2592 |
Safety & Health
- Hazardous Decomposition Products
when disposed of in fire
Nitrogen oxides and other toxic gasses and vapors.
Disposal
- Regular procedures approved by local authorities
- Handling Precautions
Forced ventilation and dust masks or respirators should be used in order to ensure that operatives do not breath in dust generated by resin, hardener or formulated powder coatings.
Mandatory and recommended industrial hygiene procedures should be followed whenever our products are being handled and processed.
Packaging & Availability
- Packaging Type
- Package
Araldite GT 7004 are available in 25 Kg. & 500 kg bags.
Storage & Handling
- Shelf life (at storage temperature between 2-30°C)
- several years
- Storage
This product has a minimum shelf life of 6 years when stored in a dry place at room temperature. If stored under warmer conditions, sintering may occur.