L & L Products L-9060 Part A

Identification & Functionality

Chemical Family: Epoxy & Epoxy Derivatives
Composite Materials Functions: Fairing Filler,
Surface Finish
Technologies: Composite Materials
Product Families: Composite Materials — Surface Finishes
Other Surface Finishes

Features & Benefits

Labeling Claims: Non-Carcinogenic
Materials Features: Cleanable,
Cost Effective,
Ease of Handling,
High Impact Resistance,
High Rigidity,
Humidity Resistant,
Light Weight,
Low Density,
Odorless
Key Attributes: Cures quickly at room temperature to maximize production efficiency

REACH compliant, does not contain any CMR substances and is very low odor

Can be used in honeycomb sandwich structures typically found in aircraft interiors for void-filling and edge sealing.

Compliant to vertical burn, smoke density and smoke toxicity accordingly to FAR & JAR 25 853 and Airbus ABD0031

Material is supplied in 400ml cartridges or pails for use with bulk pumping equipment.

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Industrial
Applications: Building & Construction — Building Materials
Pipes & Plumbing
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Automotive & Transportation — Transportation
Aerospace & Aviation
Composites End Use: Pump Parts
Product Application: L&L L-9060 should be applied in a temperature range between 20°C and 25°C.

The two components can be mixed and applied directly from the cartridge using a static mixer.L-9060 can also be used with bulk pumping and mixing equipment.

When using a cartridge, the first quantity extruded out of the nozzle should be scrapped until the color is uniform.

Once applied on the panel edge, L-9060 bead can be smoothed with a spatula for approximately 70 min. It can be sanded after 3 hours. The full cure time is reached after 24h at 23°C.

Properties

	Value	Units	Test Method / Conditions
Density	0.55 - 0.59	g/cm3	—
Extrusion Rate in Cartridge (6 bars pneumatic gun at 23°C)	52	g/min	—
Max Life-Time in Nozzle (23°C)	20	min	—
Working Time (spreading time with spatula, 23°C )	70	min	—
Sanding Time (23°C)	180	min	—
Full cure-time (23°C)	24	hours	—
Hardness (after full cure, 23°C)	50	Shore D	—
Compressive Strength (55°C)	22	MPa	ISO 604
Compressive Strength (23°C)	14	MPa	ISO 604
Compressive Strength (80°C)	6	MPa	ISO 604
Compressive Modulus (23°C)	420	MPa	ISO 604
Shear Strength (23°C)	2000	N	AITM 1-00046
Compressive Strength (after 1000h, 70°C, 85% RH , 23°C)	14	MPa	ISO 604
Water Absorption (after 1000h, 70°C ,85% RH, 23°C)	2	%	PR EN 3615
Compressive Strength (after 500h 80°C dry, 23°C)	19	MPa	ISO 604
Compressive Strength (after 500h in water at RT, 23°C)	11	MPa	ISO 604
Absorption (after 500h in water at RT, 23°C)	2.8	%	PR EN 3615
Flammability (12s vertical, Burn length)	30 mm	mm	AITM 2.0002 B
Flammability (12s vertical, After flame)	2 s	s	AITM 2.0002 B
Flammability (12s vertical, Drips time)	No drips	—	AITM 2.0002 B
Optical Smoke Density	106	Ds	AITM 2.0007 A
Smoke Toxicity (HF)	0	ppm	AITM 3.0005
Smoke Toxicity (HCl)	0	ppm	AITM 3.0005
Smoke Toxicity (HCN)	15	ppm	AITM 3.0005
Smoke Toxicity (SO2+H2S)	2	ppm	AITM 3.0005
Smoke Toxicity (CO)	210	ppm	AITM 3.0005
Smoke Toxicity (NOx)	90	ppm	AITM 3.0005

Regulatory & Compliance

Safety & Health

Health and Safety: All of our products are developed with REACH compliance substances and not CMR classified.

Packaging & Availability

Storage & Handling

Shelf Life: 18 months from date of manufacture when stored at or below 23°C (73°F)