Value | Units | Test Method / Conditions | |
Specific Gravity (Natural or representative color) | 1.33 | - | ISO 1183 |
Melt Flow Index - MFI (260°C/5 kg) | 34 | g/10 min | ISO 1133 |
Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5 - 0.7 | % | ISO 294-4 |
Molding Shrinkage - MD (Flow at 2mm) | 0.4 - 0.6 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield (5 mm/min) | 63 | MPa | ISO 527 |
Tensile Strength at Break (5 mm/min) | 58 | MPa | ISO 527 |
Rockwell Hardness | 110 | Scale R | ASTM D785 |
Tensile Modulus (5 mm/min) | 3800 | MPa | ASTM D638 |
Tensile Strain at Break (5 mm/min) | 4 | % | ISO 527-2/1A |
Flexural Strength (2 mm/min) | 100 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 4000 | MPa | ISO 178 |
Charpy Impact Strength - V-notched (23°C, 4mm) | 6 | kJ/m2 | ISO 179 1eA |
Charpy Unnotched Impact Strength (23°C, 4mm) | 85 | kJ/m2 | ISO 179 1eA |
Notched Izod Impact Strength (23°C, 4 mm) | 7 | kJ/m2 | ISO 180 1A |
Notched Izod Impact Strength (- 30°C, 4 mm) | 6 | kJ/m2 | ISO 180 1A |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 112 | °C | ISO 75-2 |
Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 129 | °C | ISO 75-2 |
Value | Units | Test Method / Conditions | |
Ash Content | 15 | % | ISO 3451 |