Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Optical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.19 | g/cm³ | ISO 1183 |
Melt Flow Rate (at 300°C, 2.16 kgf) ¹¹ | 11 | g/10 min | ASTM D1238 |
Melt Volume Rate (at 300°C, 2.16 kg) ¹¹ | 10 | cm³/10 min | ASTM D1238 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.1 | % | ISO 62 |
Mold Shrinkage (flow) ᵍ ¹¹ | 0.5 - 0.9 | % | SABIC method |
Mold Shrinkage (xflow) ᵍ ¹¹ | 0.5 - 0.9 | % | SABIC method |
Specific Gravity ¹¹ | 1.19 | — | ASTM D792 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.2 | % | ISO 62-1 |
Value | Units | Test Method / Conditions | |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 98 | MPa | ASTM D790 |
Tensile Modulus (at 50 mm/min) ¹¹ | 2150 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 124 | % | ASTM D638 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6.5 | % | ASTM D638 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 59 | MPa | ASTM D638 |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 2250 | MPa | ASTM D638 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000063 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ASTM E831 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 142 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 129 | °C | ASTM D648 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 148 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Haze (at 1 mm) | 2 | % | ASTM D1003 |
Light Transmission (at 1.0 mm) | 89 | % | ASTM D1003 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at -30°C) ¹¹ | 700 | J/m | ASTM D256 |
Izod Impact (Notched, at 23°C) ¹¹ | 910 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 12 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 290 - 340 | °C | — |
Rear - Zone 1 Temperature ⁷ | 270 - 320 | °C | — |
Middle - Zone 2 Temperature ⁷ | 280 - 330 | °C | — |
Front - Zone 3 Temperature ⁷ | 290 - 340 | °C | — |
Nozzle Temperature ⁷ | 290 - 340 | °C | — |
Mold Temperature ⁷ | 80 - 105 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 50 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 40 - 80 | % | — |
Vent Depth ⁷ | 0.025 - 0.076 | mm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94HB Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability