Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
Properties
- Flame Rating
- Filler
- Glass Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (5 mm/min) | 53 | MPa | ISO 527 |
| Tensile Strength at Break (5 mm/min) | 70 | MPa | ISO 527 |
| Rockwell Hardness | 115 | Scale R | ASTM D785 |
| Tensile Modulus (5 mm/min) | 3250 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 10 | % | ISO 527 |
| Flexural Strength (2.8 mm/min) | 85 | MPa | ISO 178 |
| Flexural Modulus (2.8 mm/min) | 3160 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 19 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 18 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.25 | - | ISO 1183 |
| Melt Flow Index - MFI (250°C/10 kg) | 33 | g/10 min | ISO 1133 |
| Melt Flow Index - MFI (300°C/1.2 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.4~0.7 | % | ISO 294-4 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.3~0.6 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 130 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 134 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 126 | °C | ISO 306 |
Regulatory & Compliance
- Certifications & Compliance