| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.15 | - | ISO 1183 |
| Melt Flow Index - MFI (220°C/10 kg) | 50 | g/10 min | ASTM D 1238 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.5 | % | ISO 294-4 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.5 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 58 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 58 | MPa | ISO 527 |
| Rockwell Hardness | 107 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2100 | MPa | ASTM D638 |
| Tensile Strain at Break (50 mm/min) | 60 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 85 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2300 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 20 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 50 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 78 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 79 | °C | ISO 75-2 |
| Vicat Softening Temperature (B/50) | 89 | °C | ISO 306 |
| Vicat Softening Temperature (B/120) | 90 | °C | ISO 306 |