Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 54 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 46 | MPa | ISO 527 |
| Rockwell Hardness | 112 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2200 | MPa | ASTM D 638 |
| Tensile Strain at Break (50 mm/min) | 78 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 75 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2250 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 45 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 45 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.12 | - | ISO 1183 |
| Melt Flow Index - MFI (250°C/10 kg) | 45 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.4~0.7 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.4~0.7 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 115 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 94 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (1.8 MPa, Annealed, 4 mm) | 106 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Annealed, 4 mm) | 119 | °C | ISO 75-2 |