LNP™ STAT-KON™ Compound JK800

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

Mold Release Agent

Fillers Included

Carbon Fiber,

Talc

Polymer Name

PC/ABS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free

Materials Features

Electrically Conductive,

Flame Retardant,

Good Mold Release,

Heat Stabilized,

High Hydrolytic Stability,

High Modulus,

High Stiffness,

High Strength,

Light Weight,

Non-brominated,

Non-chlorinated

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Industrial Automation

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Cash Dispenser (ATM),

Electrical/Electronic Applications,

Electronic Components,

Home Appliances,

Industrial Applications,

Semiconductor Applications,

Vacuum Cleaners,

Wiring Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 5VB,

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	96	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	96	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	1.9	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.9	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	7580	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	144	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	6200	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	95	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	95	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	1.9	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.9	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	7500	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	145	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	145	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6380	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.25	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.1 - 0.2	%	SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Melt Flow Rate (at 260°C, 2.16 kgf) ᵍ ¹¹	17	g/10 min	ASTM D1238

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate B/50) ¹¹	111	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	97	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	92	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	94	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000252	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000648	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.000026	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.000074	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	101	°C	ISO 306
Relative Temperature Index (Electrical) ᵖ ¹¹	60	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	60	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	60	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ᵈ ¹¹	1000	Ω.cm	ASTM D257
Surface Resistivity ᵈ ¹¹	1000000	Ω	ASTM D257
Static Decay (at 5000V to max. 50V) ¹¹	max. 0.01	Seconds	FTMS101B
Hot Wire Ignition (PLC 0) ¹¹	min. 1	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 1	mm	UL 746A

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	347	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	37	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	82	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	21	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	75 - 80	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Maximum Moisture Content ⁷	0.04	%	—
Melt Temperature ⁷	230 - 275	°C	—
Nozzle Temperature ⁷	230 - 275	°C	—
Front - Zone 3 Temperature ⁷	225 - 275	°C	—
Middle - Zone 2 Temperature ⁷	215 - 260	°C	—
Rear - Zone 1 Temperature ⁷	210 - 255	°C	—
Mold Temperature ⁷	50 - 70	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	40 - 70	rpm	—
Shot to Cylinder Size ⁷	30 - 80	%	—
Vent Depth ⁷	0.038 - 0.076	mm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 1	mm	UL 94
UL Recognized (94-5VB Flame Class Rating) ᵖ	min. 1.5	mm	UL 94
Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ	800	°C	IEC 60695-2-13
Glow Wire Flammability Index (at 1.5 mm) ᵖ	960	°C	IEC 60695-2-12

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America