Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at Yield (50 mm/min) | 60 | MPa | ISO 527 |
| Tensile Strength at Break (50 mm/min) | 80 | MPa | ISO 527 |
| Rockwell Hardness | 120 | Scale R | ASTM D785 |
| Tensile Modulus (50 mm/min) | 2300 | MPa | ASTM D 638 |
| Tensile Strain at Break (50 mm/min) | 80 | % | ISO 527-2/1A |
| Flexural Strength (2 mm/min) | 95 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2500 | MPa | ISO 178 |
| Charpy Impact Strength - V-notched (23°C, 4mm) | 50 | kJ/m2 | ISO 179 1eA |
| Charpy Impact Strength - V-notched (-30°C, 4mm) | 15 | kJ/m2 | ISO 179 1eA |
| Notched Izod Impact Strength (23°C, 4 mm) | 40 | kJ/m2 | ISO 180 1A |
| Value | Units | Test Method / Conditions | |
| Specific Gravity (Natural or representative color) | 1.15 | - | ISO 1183 |
| Melt Flow Index - MFI (250°C/2.16 kg) | 6 | g/10 min | ASTM D 1238 |
| Melt Flow Index - MFI (250°C/10 kg) | 37 | g/10 min | ISO 1133 |
| Molding Shrinkage - MD (Flow at 2mm) | 0.35~0.65 | % | ISO 294-4 |
| Molding Shrinkage - TD (Cross-Flow at 2mm) | 0.35~0.65 | % | ISO 294-4 |
| Water Absorption (23°C) | 0.1 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT (1.8 MPa, Unannealed, 4 mm) | 109 | °C | ISO 75-2 |
| Heat Deflection Temperature - HDT (0.45 MPa, Unannealed, 4 mm) | 125 | °C | ISO 75-2 |