Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Form
- Mechanical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Density (Annealed material) | 931.0 | kg/m³ | ASTM D792 / ASTM D1505 |
Tensile Stress at Yield (Tensile strength) | 22 | MPa | ASTM F648 / ASTM D638 |
Tensile Stress at Break (Ultimate tensile strength) | 55 | MPa | ASTM F648 / ASTM D638 |
Elongation (at Break) | 401.0 | % | ASTM F648 / ASTM D638 |
Shore Hardness (15 sec) | 66.0 | D - Scale | ASTM D2240 |
Notched Impact Strength (Charpy) | 101 | kJ/m² | ISO 11542.2 |
Crystallinity (1ˢᵗ heat, 20°C - 160°C) | 58.0 | % | ASTM F2625, Differential Scanning Calorimeter |
Notched Impact Strength (lzod) | 102 | kJ/m² | ASTM F648 |
Water Absorption (at 23°C until Saturation) | max. 0.05 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Melting Temperature (10°C/min) | 138.0 | °C | ASTM DF2625, Differential Scanning Calorimeter |
Vicat Softening Point (10N, at 50°C/hr) | 134.0 | °C | ASTM D1525 |
Coefficient of Linear Thermal Expansion (23°C to 80°C) | 1.8 x 10⁻⁴ | K⁻¹ | ASTM D696 |
Heat Deflection Temperature (at 1.8 MPa) | 45.0 | °C | ASTM D648 |
Thermal Conductivity | approx. 0.4 | W/(m*K) | DIN 52612 |
Crystallization Temperature Range (20°C - 160°C) | 126 - 144 | °C | ASTM F2625 |
Ash Particles | max. 150 | mg/kg | ISO 3451 -1 |
Oxidation Resistance (Surface oxidation index) | max. 0.1 | — | ASTM F2102 |
Oxidation Resistance (Bulk oxidation index) | max. 0.1 | — | ASTM F2102 |
Oxidation Induction Time to Conducted (at 200°C) | 10.0 | min | ASTM D3895 |
Regulatory & Compliance
- Quality Standards