Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Characterstics
- Elektrisch leitfähig
- Good slide properties
- For use in explosion hazard areas
- Extremely high conductivity
- Voltage dissipation on the surface in less than 0.1s
- Reduction in drive power with no reduction in performance
- Saves up to 50% energy $$ Minimal and constant sliding friction coefficient even in continuous operation
- Self-lubricating $$ Approved for use in the food industry (EU and/or FDA)
- Capabilities
As a solid sliding base in the semi-conductor industry For modular chain and conveyor belts Guides for PET bottle conveyors As workpiece carriers for sensitive electronic components Guides and slide elements for machine construction
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Average Coefficient of Friction against POM⁶ (0.25 m/s, 0.25 N/mm²) | approx. 0.18 | μ | — |
| Average Coefficient of Friction against Steel⁶ (0.25 m/s, 0.25 N/mm²) | approx. 0.1 | μ | — |
| Breaking Elongation | min. 220 | % | DIN EN ISO 5272 |
| Charpy Impact Strength (Two-sided Notch) | min. 120 | kJ/m² | DIN EN ISO 179 |
| Coefficient of Elasticity (Tensile Test) | min. 700 | MPa | DIN EN ISO 5272 |
| Hardness | 60 - 63 | Shore D | DIN EN ISO 868 |
| Indentation Hardness | min. 25 | MPa | DIN EN ISO 2039 |
| Sand-Slurry Test | 80 | % | DIN EN ISO 15527 |
| Yield Stress | approx. 20 | MPa | DIN EN ISO 5272 |
| Value | Units | Test Method / Conditions | |
| Code | PE - UHMW | — | ISO 10431 |
| Average Molecular Weight | 9 x 10⁶ | g/mol | — |
| Density | max. 0.94 | kg/dm³ | DIN EN ISO 11831 |
| Material Colour | Black | — | — |
| Sheet Group | 1.1 | — | DIN EN ISO 15527 |
| Water Absorption (Saturation at 23°C) | max. 0.01 | % | — |
| Value | Units | Test Method / Conditions | |
| Burning behavior UL 94 (Sample thickness 3/6mm) | HB/HB | — | — |
| Heat Conductivity (23°C) | 0.4 | W/(K x m) | DIN 52612 |
| Linear Thermal Coefficient of Expansion α (Average Value between 23 and 60°C) | 20 x 10⁻⁵ | m/(K x m) | DIN EN ISO 113592 |
| Lower Service Temperature⁴ | -200 | °C | — |
| Melting Temperature | 130 - 135 | °C | DIN EN ISO 3146 |
| Upper Service Temperature Constant in Air (5000h)³ | 80 | °C | — |
| Upper Service Temperature Short-term (Air)² | 90 | °C | — |
| Value | Units | Test Method / Conditions | |
| Specific Surface Resistance | max. 10⁶ | Ω | IEC 60093 |
| Specific Contact Resistance | max. 10⁻⁶ | Ω x cm | IEC 60093 |
Regulatory & Compliance
- Certifications & Compliance