It is recommended that coating application be performed in a clean environment to minimize surface defects. To make the coating solution, combine Part A and Part B at 9/1 weight ratio and mix well by stirring briefly. The coating may be applied by spraying, dipping, flowing, brushing or rolling. For spraying, an HVLP spray gun with a nozzle size of <1.0 mm is recommended; and the pressure should be set at approximately 25 to 30 psi. The induction time for spray application is 30 min, i.e., wait at least 30 minutes after mixing before coating application. For other application methods, it is recommended to age the mixed solution for at least 16 hours to obtain a highly transparent coating.
For Best Performance : Although the mixed coating solution is stable indefinitely, it is recommended to use the solution within 72 hours after mixing for best results.
Properties
- Physical Form
- Physical Properties
- Technical Data
- Abrasion Resistance
* Taber abrasion test, polycarbonate substrate, CS - 10F wheels, 500g load, 500 cycles
Value | Units | Test Method / Conditions | |
Pot Life | 72 | hours | — |
Viscosity (at 20°C, Mixed) | 10 - 25 | cP | — |
Abrasion Resistance (Δ Haze)* | max. 2 | % | ASTM D1044 Taber Abrasion Test |
Value | Units | Test Method / Conditions | |
Coverage | 700 - 1,000 | ft²/gallon | — |
Cured Film Thickness | 3 - 10 | μm | — |
Curing Temperature | Varies by substrate | °C | — |
Induction Time (For Spray Application) | 30 | minutes | — |
Mix Ratio (A:B, by weight) | 9 : 1 | — | — |
Technical Details & Test Data
- UV-Vis Spectrum on Glass
- Surface Preparation
Ensure surfaces to be coated are clean and dry and apply a primer if necessary. NEI supplies two primers for polymer substrates: SRP-50 for PMMA and SRP-51 for PC. The primer may be applied by dipping, flowing, spinning, rolling or spraying.
For spraying, an HVLP spray gun with a nozzle size of <1.0 mm is recommended, and the pressure should be set at approximately 25 to 30 psi. A single pass of spraying is recommended for the primer. The primed parts should be dried at 80ºC for 10 min before application of NANOMYTE® UVP-100.- Curing Conditions
- NANOMYTE® UVP-100 is thermally cured at an elevated temperature. Recommended curing conditions :
- PMMA: 2 hours at 80°C
- Polycarbonate, ABS, PC-ABS: 1 hour at 100 – 120°C (depending on heat distortion temperature)
- Other: 30 minutes at 150°C for substrates that can withstand high temperatures
- Shorter cure times / reduced temperatures may also be used depending on surface properties and performance requirements; test samples for desired performance when deviating from recommendations.
- Clean Up
Clean tools and flush equipment thoroughly with water followed by isopropyl alcohol or acetone before product dries. Once coating is dry, the tools will not clean with acetone or any other solvent.
Packaging & Availability
- Available Quantities
NANOMYTE® UVP-100 is a 2-part coating, sold in liter or gallon kit quantities.
UVP-100 1 Liter Kit 1 Gallon Kit 5 Gallon Kit (Part A) 900 grams 3420 grams 17.1 kg (Part B) 100 grams 380 grams 1.9 kg
Storage & Handling
- Storage and Handling
Precautions for Safe Handling
Appropriate personal protective equipment should be used at all times. Provide good ventilation or extraction. Avoid contact with eyes, skin, and clothing. Avoid inhalation of vapor or mist. Keep away from heat, sparks, flames and other sources of ignition. No smoking. Take measures to prevent the build-up of electrostatic charge.
Conditions for Safe Storage
For best coating performance, keep Parts A and B unmixed until ready to use. Keep containers tightly sealed and store in a dry and cool area. Opened containers must be carefully resealed and kept upright to prevent leakage. Keep away from sources of ignition. Part A may form explosive peroxides on prolonged storage. Storage class (TRGS 510): 3: Flammable liquids