Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Prepolymer
- Aliphatic Polyether
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- KEY BENEFITS
• Seamless monolithic • Corrosion resistance
• Additives – color, UV stabilizer, anti-static
• Any climate • Reduced bridging
Applications & Uses
- Markets
- SURFACE PREPARATION
Grit-blast using standard SSPC-SP10 near white including minimum 50 micron (0.002”) angular depth profile for maximum adhesion or mechanically roughen using standard SSPC-SP11 to achieve desired adhesion strength. Primers must always be used.
Primers: NP-9500: Metal or Polyurethane
NP-9600: Metal immersion service with NP-9500.
NP-100: Concrete- APPLICATION DATA (23°C / 73°F)
Mix Ratio: 100A: 27B by weight
Temperature: 7°C to 40°C (45°F to 104°F)
Dilution: Dichloromethane, Methyl Ethyl Ketone
Working Time: >1 hour
Tack free: 1 hour
Recoat Time: 15 minutes, maximum 72 hours
Light duty service: 24 hours
Ultimate cure: 5 days
Clean up: Non-oil-based solvent
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Hardness | 55 - 65 | Shore D | - |
| Theoretical Coverage (25 micron/kg (94.88 sqft at. 001”/lb)) | 19.44 | sqm | - |
| Solids Content | 56.93 | % | - |
| Flash Point | -9.0 | °C | - |
| Tensile Strength | 35.16 (5100 ) | - | ASTM D412 |
| Elongation | 220.0 | % | ASTM D412 |
| Tear Strength | 91.94 (525 ) | kN/m(lb-in) | ASTM D624 Die C |
| Taber Abrasion 1kf, 1000cy, H-18 | 90 loss | mg | ASTM D4060-19 |
| Impact Resistance | max. 28.02 (160 ) | kN/m(pli) | ASTM D2794 |
| Operating Temperatures | -56(-70)-93(200) | °C(°F) | - |
| Immersion Operating Temp | Max 60 (140) | °C(°F) | - |
| Vapor Transmission | min. 0.10 | - | ASTM E96-80 |
| Transportation | DGR | - | - |
Packaging & Availability
- Available Kit Sizes
1 kg, 5 kg, 25.4 kg, 275 kg
Storage & Handling
- Storage
Shelf Life: 2 years unopened
Storage: 23°C/73°F, dry away from sunlight