- Two-part, low viscosity clear RTV silicone
- Based on a dimethyl-diphenyl copolymer with a broad operating temperature range
- 10:1 Mix Ratio (Part A:B)
Applications & Uses
- Markets
- Plastics & Elastomers Processing Methods
- Applications
- For bonding, casting or injection molding of high performance optical components
- For applications requiring index matching at 1.43
- For photonics applications requiring low outgassing and minimal volatile condensables to avoid condensation in sensitive devices
- For applications requiring an operating temperature range of -115°C to 260°C (-178°F to 500°F)
- Instructions for Use
Mixing
Thoroughly mix Part A and Part B, in a 10:1 mix ratio by weight prior to use.
Deaeration
The assembly should self-deaerate due to the product’s long room temperature work time and low viscosity, as long as no pockets of air are trapped beneath mechanical parts. If accelerated deaeration is required, the assembly may be vacuum deaerated using a pressure of 635 mmHg (25 inHg) or greater. Apply the vacuum while observing the uncured fluid for presence of bubble formation and increase vacuum slowly enough to avoid rapid foaming. Hold vacuum until bubbles at the fluid surface collapse and are no longer visible.
Cure Inhibition
LS-6143 cures in contact with most properly cleaned substrate materials including optical glasses, optical plastics, and photonic semiconductors. Adhesion to fluoroplastic substrates is generally poor but may be improved with chemical etching or plasma etching of the substrate. Substrates to avoid include certain butyl, nitrite, chlorinated, and EPDM elastomers, certain plastics with leachable plasticizers, and the cure residues of certain adhesives including UV-cured epoxies and amine-cured epoxies.
Substrate Preparation
Substrates should be free of dust, oil, and fingerprint soils. Clean substrates using suitable industrial techniques for cleaning electro-optics. If using hydrocarbon solvent cleaning (e.g. acetone, toluene), a final rinse with reagent grade isopropanol is recommended. If using aqueous detergent cleaning, multiple final rinses with de-ionized water or a single rinse with reagent grade isopropanol is recommended. Obtain improved gel adhesion to some substrates using suitable primers such as NuSil Technology LS series Optical Primers. Adhesion to fluoroplastic substrates is generally poor but may be improved with chemical etching or plasma etching of the substrate.
Adjustable Cure
Schedule Product cures at a wide range of cure times and temperatures to accommodate different production needs. Contact NuSil Technology for details. Cure schedules* include:
65°C (149°F) /15 minutes
100°C (212°F) /1 minute
Clean-up
Remove from surfaces by first wiping off excess gel with a suitable, dry, lint-free wipe and then by wiping down the surface with a lint-free wipe soaked with acetone. If the surface material is incompatible with acetone, use isopropanol. Complete the clean-up process with a final rinse with reagent grade isopropanol if removal of acetone residues is necessary. The user is responsible for compliance with all applicable regulations governing disposal of waste materials as indicated in the MSDS.
Properties
- Appearance
- Translucent
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Viscosity | 5,500 (5,500 ) | cP (Mpa*s) | — |
| Durometer Type A | 40.0 | — | — |
| Tensile | 600 (4.14 ) | psi (MPa) | — |
| Elongat ion | 125.0 | % | — |
| Cte | 10.0 | ppm/°C | — |
| Dielectric Strength | 550 (21.45 ) | volts/mil (kV/mm) | — |
| Ionic Content Cl | max. 5 | ppm | — |
| Ionic Content K | max. 1 | ppm | — |
| Ionic Content Na | max. 1 | ppm | — |
| Lap Shear | 180 (1.24 ) | psi (MPa) | — |
| Mix Rat io | 0.417361111 | — | — |
| Refractive Index | 1.43 | — | — |
| Specific Gravity | 1.04 | — | — |
| Volume Resistivity | 1.10E+15 | ohmcm | — |
| Work Time | 2.0 | hours | — |
| Value | Units | Test Method / Conditions | |
| Cure System | Platinum | — | — |
| Cure at 65 °C | 4.0 | hours | — |