Plastifloor® 800 N is a viscous elasticized PU-MMA hybrid resin with especially high flexibility at very low-temperatures. This resin may be used for constructing membranes and coatings in coolers and freezers as well as for liquid waterproofing and as a joint filler. Together with our PET/SL filler that has been especially developed for this type of resin, the coating will stay more elastic, even at low temperatures. Thus the resin can be used for car park coatings, bridge deck overlays and pool coatings. The resin can be used also for roofing, inlets and to protect dome lights.
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Processing Notes
Suggested formulation:
Plastifloor® 800 N can be filled as described below with fillers and pigments for producing a coating mass that is ready for application.
800 N/1
Membrane Layer 1 - 2 mm:
- 80 ppW Plastifloor® 800 N
- 20 ppW Plastifloor® Quartz powder 1600
800 N/2
Coating, broadcast 5 - 8 mm:- 50 ppW Plastifloor® 800 N
- 24 ppW Plastifloor® Quartz powder 1600
- 24 ppW Quartz sand 20 - 40 mesh
- 2 ppW Pigment powderx
800 N/3
Joint grouting:- 80 ppW Plastifloor® 800 N
- 15 ppW Plastifloor® Quartz powder 1600
- 5 ppW Pigment powder
800 N/4
Waterproofing membrane:- 60 ppW Plastifloor® 800 N
- 40 ppW Plastifloor® Quartz powder 1600
Add 3 - 4 Vol.-% Plastifloor® Hardener 50 W to each formula
Processing:
Recipe 800 N/1 is applied to the substrate, pre-primed with Plastifloor® 112 N or 113 N by using a notched trowel made of metal or MMA durable plastic. Recipe 800 N/2 is pre-dispersed by a pin squeegee and evened by a smoothing trowel. This formulation is especially suitable for floors in coolers and freezers (down to - 86°F). For increasing the pressure resistance and grip, the flow coating is being broadcasted to excess with quartz sand - size 15 - 35 mesh. Remove the surplus sand before applying the topcoat. Plastifloor® 800 N coatings should be sealed with Plastifloor® 528 N (clear or pigmented) or followed by another coating layer. Recipe 800 N/3 is used for casting interior and exterior pre-primed movement joints. Especially observe the fact that the casting compound will only form a compound on the joint‘s side flanks if this has carefully been primed with Plastifloor® 112 N. In recipe 800 N/4 the resin Plastifloor® 800 N is mixed with filler 800 PET. It serves for producing highly elastic, waterproof sealing layers on car park decks, balconies, roofs and terraces. The Plastifloor® 800 N resin and filler 800 PET mix is applied to the surface that has been primed with Plastifloor® 112 N, then compounded by a polyester fleece and coated wet-in-wet.
Pot life and curing times depending on temperature:
Further coating layers with Plastifloor® must only be applied after the previous layers have completely cured.
Temperature [°F] Hardener [Vol-%] Pot life [min] Curing time [min]
41 5 approx. 25 approx. 70 50 4 approx. 25 approx. 60 68 3 approx. 20 approx. 45 86 2 approx. 25 approx. 50 Thinner:Up to 5 Vol.-% Plastifloor® Accelerator 440
Processing below 32°F:Please use Plastifloor® Accelerator B101! Dosage according to data sheet Plastifloor® Accelerator B101.
Properties
- Color
- Physical Form
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Flow time (68°F) | 53 - 68 | sec | DIN flow cup, 6mm |
| Curing (68°F) | min. 45 - 60 | minute | — |
| Density (68°F) | 8.5123 | lb/gal | ISO 2811 |
| Flashpoint | 50.0 | °F | DIN 51755 |
Packaging & Availability
- Bundle
- 396.83 lb drums
- 55.12 lb, 22.05 lb pails.
Storage & Handling
- Shelf life
In the original container, dark at < 65°F maximum 6 months.
- Storage
The handling-regulations for highly flammable materials apply to methacrylate resins. Plastifloor® resins are to be stored cool, protected against direct sunlight and preferably at temperatures of 59 - 68 °F. During storage paraffin – particles and filler – materials may precipitate. Thus before processing, containers have to be stirred up well.