Value | Units | Test Method / Conditions | |
Apparent Density | 0.93 | g/cm³ | ASTM D1895 |
Coefficient of Thermal Expansion | 2.8e-05 | per °C | ASTM E831 |
Compressive Strength | 142 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 180 | °C | ASTM D648 |
Flexural Modulus | 12958 | MPa | ASTM D790 |
Flexural Strength | 72.4 | MPa | ASTM D790 |
Heat Resistance | 257 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 37 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 14.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 16 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0043 | m/m | ASTM D6289 |
Oxygen Index | 41.2 | % | ASTM D2863 |
Post Shrinkage (at 120°C, 72hr) | 0.09 | % | ASTM D6289 |
Rockwell Hardness | 110 | M scale | ASTM D785 |
Specific Gravity | 1.74 | — | ASTM D792 |
Tensile Elongation | 0.3 | % | ASTM D638 |
Tensile Modulus | 15612 | MPa | ASTM D638 |
Tensile Strength | 42 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 1.94 | W/m/°C | ASTM E1461 |
Water Absorption | 0.05 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.92 | g/cm³ | ASTM D1895 |
Coefficient of Thermal Expansion | 2.8e-05 | per °C | ASTM E831 |
Compressive Strength | 144 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 194 | °C | ASTM D648 |
Flexural Modulus | 13303 | MPa | ASTM D790 |
Flexural Strength | 63.3 | MPa | ASTM D790 |
Heat Resistance | 250 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 35 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 14.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 16.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0023 | m/m | ASTM D6289 |
Oxygen Index | 41.2 | % | ASTM D2863 |
Post Shrinkage (at 120°C, 72hr) | 0.07 | % | ASTM D6289 |
Rockwell Hardness | 109 | E scale | ASTM D785 |
Specific Gravity | 1.74 | — | ASTM D792 |
Tensile Elongation | 0.2 | % | ASTM D638 |
Tensile Modulus | 15211 | MPa | ASTM D638 |
Tensile Strength | 31 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 1.94 | W/m/°C | ASTM E1461 |
Water Absorption | 0.05 | % | ASTM D570 |