Plastics Engineering Company 06343 Two-Stage Phenolic

Identification & Functionality

Chemical Family: Phenol Formaldehyde (PF),
Phenols & Phenolics
Polymer Name: Phenol Formaldehyde (PF)
Reinforcement Material: Glass Fibers
Composite Materials Functions: Molding Compound
Technologies: Composite Materials
Product Families: Composite Materials — Prepregs & Molding Compounds
Other Prepregs & Molding Compounds

Features & Benefits

Materials Features: Excellent Surface Hardness,
Good Electrical Properties,
Heat Resistance,
High Tensile Strength,
Two-Stage,
UL Listed,
Wear Resistant

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Electrical & Electronics,
Industrial,
Printing & Packaging
Applications: Automotive & Transportation — Automotive
Chassis & Brake,
Powertrain & UTH
Building & Construction — Building Materials
Pipes & Plumbing
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Industrial — Military & Defense
Advanced Materials
Industrial — Oil, Gas & Mining
Exploration & Upstream
Printing & Packaging — Packaging
Healthcare Packaging
Electrical & Electronics — Parts & Components
Housings & Enclosures,
Terminal Blocks, Plugs & Sockets
Automotive & Transportation — Transportation
Aerospace & Aviation,
Commercial
Composites End Use: Aerospace Applications,
Brake Pads,
Cases,
Housings
Composites Processing Methods: Compression Molding
Plastics & Elastomers Processing Methods: Transfer Molding

Properties

	Value	Units	Test Method / Conditions
Apparent Density	0.85	g/cm³	ASTM D1895
Arc Resistance	188	sec	ASTM D495
Coefficient of Thermal Expansion	2.6e-05	per °C	ASTM E831
Comparative Tracking Index	200	V	ASTM D3638
Compressive Strength	169	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	190	°C	ASTM D648
Dielectric Strength (Short Time)	17.7	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.017	—	ASTM D150
Flexural Modulus	12074	MPa	ASTM D790
Flexural Strength	54.8	MPa	ASTM D790
Heat Resistance	225	°C	ASTM D794
Impact Strength (Drop Ball)	69	J/m	Plenco
Impact Strength (Notched, Izod)	16.6	J/m	ASTM D256
Impact Strength (Notched, Charpy)	18.3	J/m	ASTM D256
Mold Shrinkage *	0.0029	m/m	ASTM D6289
Oxygen Index	42.7	%	ASTM D2863
Permittivity (at 1MHz)	4.6	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.04	%	ASTM D6289
Rockwell Hardness	71	E-Scale	ASTM D785
Specific Gravity	1.73	—	ASTM D792
Tensile Elongation	0.3	%	ASTM D638
Tensile Modulus	15627	MPa	ASTM D638
Tensile Strength	40	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.55	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	15000000000000	ohm·cm	ASTM D257
Water Absorption	0.05	%	ASTM D570

	Value	Units	Test Method / Conditions
Apparent Density	0.81	g/cm³	ASTM D1895
Arc Resistance	180	sec	ASTM D495
Coefficient of Thermal Expansion	2.6e-05	per °C	ASTM E831
Comparative Tracking Index	187	V	ASTM D3638
Compressive Strength	174	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	186	°C	ASTM D648
Dielectric Strength (Short Time)	18.4	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.035	—	ASTM D150
Flexural Modulus	14253	MPa	ASTM D790
Flexural Strength	87.2	MPa	ASTM D790
Heat Resistance	217	°C	ASTM D794
Impact Strength (Drop Ball)	86	J/m	Plenco
Impact Strength (Notched, Izod)	17.8	J/m	ASTM D256
Impact Strength (Notched, Charpy)	21.6	J/m	ASTM D256
Mold Shrinkage *	0.0034	m/m	ASTM D6289
Oxygen Index	42.7	%	ASTM D2863
Permittivity (at 1MHz)	4.9	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.05	%	ASTM D6289
Rockwell Hardness	77	E-Scale	ASTM D785
Specific Gravity	1.73	—	ASTM D792
Tensile Elongation	0.3	%	ASTM D638
Tensile Modulus	15150	MPa	ASTM D638
Tensile Strength	43	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.55	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	5300000000000	ohm·cm	ASTM D257
Water Absorption	0.04	%	ASTM D570