Plastics Engineering Company 06401 Two-stage Phenolic

Identification & Functionality

Chemical Family: Phenol Formaldehyde (PF),
Phenols & Phenolics
Polymer Name: Phenol Formaldehyde (PF)
Reinforcement Material: Glass Fibers,
Mineral
Composite Materials Functions: Molding Compound
Technologies: Composite Materials
Product Families: Composite Materials — Prepregs & Molding Compounds
Other Prepregs & Molding Compounds

Features & Benefits

Materials Features: Excellent Surface Hardness,
Heat Resistance,
High Tensile Strength,
Two-Stage,
UL Listed,
Wear Resistant

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Electrical & Electronics,
Industrial,
Printing & Packaging
Applications: Automotive & Transportation — Automotive
Chassis & Brake,
Powertrain & UTH
Building & Construction — Building Materials
Pipes & Plumbing
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Industrial — Military & Defense
Advanced Materials
Industrial — Oil, Gas & Mining
Exploration & Upstream
Printing & Packaging — Packaging
Healthcare Packaging
Electrical & Electronics — Parts & Components
Housings & Enclosures,
Terminal Blocks, Plugs & Sockets
Automotive & Transportation — Transportation
Aerospace & Aviation,
Commercial
Composites End Use: Aerospace Applications,
Brake Pads,
Cases,
Housings
Composites Processing Methods: Compression Molding,
Injection Molding
Plastics & Elastomers Processing Methods: Transfer Molding

Properties

	Value	Units	Test Method / Conditions
Apparent Density	0.67	g/cm³	ASTM D1895
Arc Resistance	74	sec	ASTM D495
Coefficient of Thermal Expansion	3.8e-05	per °C	ASTM E831
Comparative Tracking Index	175	V	ASTM D3638
Compressive Strength	238	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	209	°C	ASTM D648
Dielectric Strength (Short Time)	14.3	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.03	—	ASTM D150
Flexural Modulus	14241	MPa	ASTM D790
Flexural Strength	165.5	MPa	ASTM D790
Heat Resistance	220	°C	ASTM D794
Impact Strength (Drop Ball)	292	J/m	Plenco
Impact Strength (Notched, Charpy)	36.1	J/m	ASTM D256
Impact Strength (Notched, Izod)	39.9	J/m	ASTM D256
Mold Shrinkage *	0.0023	m/m	ASTM D6289
Permittivity (at 1MHz)	4.7	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.07	%	ASTM D6289
Rockwell Hardness	96	E-Scale	ASTM D785
Specific Gravity	1.72	—	ASTM D792
Tensile Elongation	0.7	%	ASTM D638
Tensile Modulus	15144	MPa	ASTM D638
Tensile Strength	86	MPa	ASTM D638
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	960000000000	ohm·cm	ASTM D257
Water Absorption	0.08	%	ASTM D570

	Value	Units	Test Method / Conditions
Apparent Density	0.75	g/cm³	ASTM D1895
Arc Resistance	104	sec	ASTM D495
Coefficient of Thermal Expansion	3.8e-05	per °C	ASTM E831
Comparative Tracking Index	180	V	ASTM D3638
Compressive Strength	255	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	228	°C	ASTM D648
Dielectric Strength (Short Time)	15.2	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.025	—	ASTM D150
Flexural Modulus	13478	MPa	ASTM D790
Flexural Strength	121.7	MPa	ASTM D790
Heat Resistance	227	°C	ASTM D794
Impact Strength (Drop Ball)	273	J/m	Plenco
Impact Strength (Notched, Izod)	39.3	J/m	ASTM D256
Impact Strength (Notched, Charpy)	39.4	J/m	ASTM D256
Mold Shrinkage *	0.0014	m/m	ASTM D6289
Permittivity (at 1MHz)	5.2	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.05	%	ASTM D6289
Rockwell Hardness	98	E-Scale	ASTM D785
Specific Gravity	1.75	—	ASTM D792
Tensile Elongation	0.6	%	ASTM D638
Tensile Modulus	14720	MPa	ASTM D638
Tensile Strength	73	MPa	ASTM D638
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	3100000000000	ohm·cm	ASTM D257
Water Absorption	0.07	%	ASTM D570

	Value	Units	Test Method / Conditions
Apparent Density	0.74	g/cm³	ASTM D1895
Arc Resistance	76	sec	ASTM D495
Coefficient of Thermal Expansion	3.8e-05	per °C	ASTM E831
Comparative Tracking Index	175	V	ASTM D3638
Compressive Strength	274	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	273	°C	ASTM D648
Dielectric Strength (Short Time)	14.3	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.035	—	ASTM D150
Flexural Modulus	16440	MPa	ASTM D790
Flexural Strength	192.5	MPa	ASTM D790
Heat Resistance	228	°C	ASTM D794
Impact Strength (Drop Ball)	343	J/m	Plenco
Impact Strength (Notched, Charpy)	47.7	J/m	ASTM D256
Impact Strength (Notched, Izod)	50.1	J/m	ASTM D256
Mold Shrinkage *	0.0012	m/m	ASTM D6289
Permittivity (at 1MHz)	5.4	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.05	%	ASTM D6289
Rockwell Hardness	99	E-Scale	ASTM D785
Specific Gravity	1.74	—	ASTM D792
Tensile Elongation	0.8	%	ASTM D638
Tensile Modulus	15952	MPa	ASTM D638
Tensile Strength	110	MPa	ASTM D638
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	620000000000000	ohm·cm	ASTM D257
Water Absorption	0.08	%	ASTM D570

Regulatory & Compliance

Knowde Enhanced TDS