Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Markets
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.7 | g/cm³ | ASTM D1895 |
Arc Resistance | 154 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 184 | V | ASTM D3638 |
Compressive Strength | 209 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 198 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.031 | — | ASTM D150 |
Flexural Modulus | 12586 | MPa | ASTM D790 |
Flexural Strength | 124.9 | MPa | ASTM D790 |
Heat Resistance | 194 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 198 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 28.4 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 33.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0034 | m/m | ASTM D6289 |
Oxygen Index | 34.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.1 | % | ASTM D6289 |
Rockwell Hardness | 95 | E-Scale | ASTM D785 |
Specific Gravity | 1.76 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 13382 | MPa | ASTM D638 |
Tensile Strength | 79 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.54 | W/m/°C | ASTM E1461 |
UL Flammability (at 3mm) | V-0 | — | UL 94 |
Volume Resistivity | 790000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.1 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.7 | g/cm³ | ASTM D1895 |
Arc Resistance | 136 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 243 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 224 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 17.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.033 | — | ASTM D150 |
Flexural Modulus | 14507 | MPa | ASTM D790 |
Flexural Strength | 145 | MPa | ASTM D790 |
Heat Resistance | 196 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 230 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 37 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 38.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0012 | m/m | ASTM D6289 |
Oxygen Index | 34.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.04 | % | ASTM D6289 |
Rockwell Hardness | 99 | E-Scale | ASTM D785 |
Specific Gravity | 1.76 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 14330 | MPa | ASTM D638 |
Tensile Strength | 92 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.54 | W/m/°C | ASTM E1461 |
UL Flammability (at 3mm) | V-0 | — | UL 94 |
Volume Resistivity | 660000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.1 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance