Value | Units | Test Method / Conditions | |
Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
Arc Resistance | 134 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.4e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 189 | V | ASTM D3638 |
Compressive Strength | 115 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 233 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.085 | — | ASTM D150 |
Flexural Modulus | 8439 | MPa | ASTM D790 |
Flexural Strength | 88 | MPa | ASTM D790 |
Heat Resistance | 244 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 281 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 33 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 38.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0025 | m/m | ASTM D6289 |
Oxygen Index | 36.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.13 | % | ASTM D6289 |
Rockwell Hardness | 42 | E-Scale | ASTM D785 |
Specific Gravity | 1.59 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9392 | MPa | ASTM D638 |
Tensile Strength | 55 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | — | UL 94 |
Volume Resistivity | 640000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.17 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.4e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 157 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 245 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.2 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.077 | — | ASTM D150 |
Flexural Modulus | 8973 | MPa | ASTM D790 |
Flexural Strength | 115.4 | MPa | ASTM D790 |
Heat Resistance | 233 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 296 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 45.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 47.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0011 | m/m | ASTM D6289 |
Oxygen Index | 36.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.8 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.07 | % | ASTM D6289 |
Rockwell Hardness | 45 | E-Scale | ASTM D785 |
Specific Gravity | 1.6 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9963 | MPa | ASTM D638 |
Tensile Strength | 74 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | — | UL 94 |
Volume Resistivity | 630000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.15 | % | ASTM D570 |