- Coupling agent for fillers and reinforcements in HDPE like wood plastic composites(WPC’s).
- Chemical coupling agent for fillers like calcium carbonate, talc, mica & glass fibers in HDPE matrix.
- Wetting & Dispersing agent for colors and pigments in PE compounds.
- Processing Conditions
- A slight pungent order is normal during processing of OPTIM® E-156.
- During processing, the compounding parameters that can lead to optimized performance include extruder type, screw design, barrel temperature, screw speed, throughput, residence time and material feeding sequence.
- Maximum processing temperature should not generally exceed 280°C.
Properties
- Physical Form
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Hardness
Value | Units | Test Method / Conditions | |
Tensile Strength | 11 | MPa | ASTM D638/2010 |
Percentage Elongation | 10 | % | ASTM D638/2010 |
Tensile Modulus | 50 | MPa | ASTM D638/2010 |
Flexural Modulus | 670 | MPa | ASTM D790/2010 |
Flexural Strength | 20 | MPa | ASTM D790/2010 |
Value | Units | Test Method / Conditions | |
Melting Temperature | 129 | °C | DSC |
Vicat Softening Temperature | 121 | °C | ASTM 1525/2010 |
Value | Units | Test Method / Conditions | |
MFI (at 190°C/2.16 Kg) | 7 | g/10min | ASTM D1238 |
Density | 0.953 | g/cm³ | ASTM D792 |
Bulk Density | 0.55 | g/ml | PLUSS® method |
Bonded Maleic Anhydride | Medium | — | PLUSS® method |
Value | Units | Test Method / Conditions | |
Durometer Hardness | 60 | Shore D | ASTM D2240/2004 |
Packaging & Availability
- Packaging Type
- Packaging Information
- OPTIM® speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC’s.
- They should be stored in cool and dry place.
Storage & Handling
- Storage and Handling Procedures
- OPTIM® E-156 should be stored away from heat, sparks and flame.
- It should be kept in a cool, dry & well ventilated place.
- It is recommended that prior to processing, the requisite quantity of material to be used should be dried in a hopper dryer or oven at 80-95°C for about 2 hours for obtaining best results.