| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 10 | MPa | ISO 527-2 |
| Hardness (15 s) | 40 | Shore D | D2240 |
| Elongation at Yield | 9 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 450 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 27 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Index - MFI (230°C/2.16kg) | 8 | g/10min | ISO 1133 |
| Density | 0.91 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.8 - 2.2 | % | ISO 294-4 |
| Molding Shrinkage - Across Flow | 1.8 - 2.2 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 50 | °C | ISO 75/1 |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 100 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 70 - 80 | °C | — |
| Back Pressure | 60 - 100 | bar | — |
| Melt Temperature | 205 - 250 | °C | — |
| Mold Temperature | 40 - 60 | °C | — |
| Peripherical Screw Speed | 650 - 800 | mm/s | — |
| Drying Time | 2.0 - 4 | h | — |