Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Filler Content
- 13 - 17
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 24 | MPa | ISO 527-2 |
| Flexural Strength | max. 36 | MPa | ISO 178 |
| Elongation at Yield | 9 | % | ASTM D 638 |
| Elongation at Break | 160 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 2300 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (-20°C) | NB | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength (-20°C) | 5 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Index - MFI (230°C/2.16kg) | 25 | g/10min | ISO 1133 |
| Density | 0.98 | g/cm³ | ISO 1183/A |
| Molding Shrinkage - Flow | 0.8 - 1.0 | % | ISO 294-4 |
| Molding Shrinkage - Across Flow | 0.8 - 1.0 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 130 | °C | ISO 306 |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 100 | °C | ISO 75/1 |
| Heat Distortion Temperature A (120°C/h at 1820kPa) | 57 | °C | ISO 75/1 |
| Vicat Softening Tempurature B (50°C/h at 49,05N) | 53 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion | 55 - 65 | 10E-6/°C | Polykemi |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 70 - 80 | °C | — |
| Drying Time | 2 - 4 | h | — |
| Back Pressure | 60 - 100 | bar | — |
| Melt Temperature | 205 - 260 | °C | — |
| Mold Temperature | 40 - 80 | °C | — |
| Peripherical Screw Speed | 600 - 750 | mm/s | — |