Properties
- Filler Content
- 8 - 12
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Strength | max. 19 | MPa | ISO 527-2 |
Flexural Strength | max. 25 | MPa | ISO 178 |
Hardness (15 s) | 54 | Shore D | D2240 |
Elongation at Yield | 8 | % | ASTM D 638 |
Flexural Modulus (23°C) | 750 | MPa | ISO 178 |
Charpy Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (23°C) | 28 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (-20°C) | NB | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (-20°C) | 15 | kJ/m² | ISO 179 |
Value | Units | Test Method / Conditions | |
Melt Flow Index - MFI (230°C/2.16kg) | 12 | g/10min | ISO 1133 |
Density | 0.96 | g/cm³ | ASTM D1505 |
Molding Shrinkage - Flow | 1.2 - 1.4 | % | ISO 294-4 |
Molding Shrinkage - Across Flow | 1.2 - 1.4 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature B (120°C/h at 455kPa) | 88 | °C | ISO 75/1 |
Vicat Softening Tempurature A (50°C/h at 9,81N) | 132 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 - 80 | °C | — |
Drying Time | 2 - 4 | h | — |
Back Pressure | 60 - 100 | bar | — |
Melt Temperature | 205 - 260 | °C | — |
Mold Temperature | 40 - 80 | °C | — |
Peripherical Screw Speed | 600 - 750 | mm/s | — |