Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Properties
- Filler Content
- 13 - 17
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
- Additional Information
Value | Units | Test Method / Conditions | |
Tensile Strength | max. 24 | MPa | ISO 527-2 |
Flexural Strength | max. 37 | MPa | ISO 178 |
Elongation at Yield | 7 | % | ASTM D 638 |
Elongation at Break | 55 | % | ASTM D 638 |
Flexural Modulus (23°C) | 1800 | MPa | ISO 178 |
Charpy Unnotched Impact Strength (23°C) | NB | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (-20°C) | 4 | kJ/m² | ISO 179 |
Charpy Unnotched Impact Strength (-20°C) | NB | kJ/m² | ISO 179 |
Value | Units | Test Method / Conditions | |
Melt Flow Index - MFI (230°C/2.16kg) | 6 | g/10min | ISO 1133 |
Density | 1 | g/cm³ | ISO 1183 |
Molding Shrinkage - Flow | 0.9 - 1.1 | % | ISO 294-4 |
Molding Shrinkage - Across Flow | 0.9 - 1.1 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature B (120°C/h at 455kPa) | 123 | °C | ISO 75/1 |
Heat Distortion Temperature A (120°C/h at 1820kPa) | 66 | °C | ISO 75/1 |
Vicat Softening Tempurature A (50°C/h at 9,81N) | 139 | °C | ISO 306 |
Vicat Softening Tempurature B (50°C/h at 49,05N) | 63 | °C | ISO 306 |
Coefficient of Linear Thermal Expansion | 60 - 80 | 10E-6/°C | Polykemi |
Value | Units | Test Method / Conditions | |
Drying Temperature | 70 - 80 | °C | - |
Drying Time | 2 - 4 | h | - |
Back Pressure | 60 - 100 | bar | - |
Melt Temperature | 205 - 260 | °C | - |
Mold Temperature | 40 - 80 | °C | - |
Peripherical Screw Speed | 600 - 750 | mm/s | - |
Value | Units | Test Method / Conditions | |
Scratch resistance - 10 N Fine structure | 0.12 | dL | ISO 1518/D65 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability