Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 HB
- Filler Content
- 28 - 32
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Parameters
Value | Units | Test Method / Conditions | |
Moisture Content | max. 0.2 | % | - |
Molding Shrinkage - Flow | 0.3 | % | ISO 294-4 |
Molding Shrinkage - Across Flow | 1.2 | % | ISO 294-4 |
Density | 1.52 | g/cm³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Tensile Strength | max. 150 | MPa | ISO 527-2 |
Flexural Strength | max. 180 | MPa | ISO 178 |
Elongation at Break | 2.5 | % | ASTM D 638 |
Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
Charpy Notched Impact Strength (23°C) | 7 | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (-20°C) | 5 | kJ/m² | ISO 179 |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature B (120°C/h at 455kPa) | 220 | °C | ISO 75/1 |
Heat Distortion Temperature A (120°C/h at 1820kPa) | 210 | °C | ISO 75/1 |
Vicat Softening Tempurature B (50°C/h at 49,05N) | 215 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Glow Wire Flammability Index - GWFI (2 mm) | 750 | °C | IEC 60695-2-12 |
UL-94 Flammability (1.6 mm) | HB | - | UL94 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 120 | °C | - |
Back Pressure | 60 - 100 | bar | - |
Drying Time | 2 - 8 | h | - |
Mold Temperature | 80 - 100 | °C | - |
Melt Temperature | 250 - 270 | °C | - |
Peripherical Screw Speed | 250 - 300 | mm/s | - |