Properties
- Filler Content
- 18 - 22
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Moisture Content | max. 0.02 | % | — |
| Molding Shrinkage - Flow | 0.3 | % | ISO 294-4 |
| Molding Shrinkage - Across Flow | 1.1 | % | ISO 294-4 |
| Melt Flow Index - MFI (275°C/2.16kg) | 48 | g/10min | ISO 1133 |
| Density | 1.39 | g/cm³ | ISO 1183/A |
| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 100 | MPa | ISO 527-2 |
| Flexural Strength | max. 156 | MPa | ISO 178 |
| Elongation at Yield | 4 | % | ASTM D 638 |
| Elongation at Break | 4 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 6200 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 7 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength (-20°C) | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 52 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (-30°C) | 32 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 215 | °C | ISO 306 |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 215 | °C | ISO 75/1 |
| Heat Distortion Temperature A (120°C/h at 1820kPa) | 195 | °C | ISO 75/1 |
| Vicat Softening Tempurature B (50°C/h at 49,05N) | 195 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 90 | °C | — |
| Back Pressure | 60 - 100 | bar | — |
| Drying Time | 2 - 8 | h | — |
| Melt Temperature | 235 - 250 | °C | — |
| Mold Temperature | 70 - 90 | °C | — |
| Peripherical Screw Speed | 300 - 400 | mm/s | — |