Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- High reactivity
- Clear unaccelerated
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 64 - 66 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 3 rpm 20 | 1100 - 1250 | mPa.s | MT-CU025V |
| Curing Time at 130°C + 1% TBPB | 175 - 205 | sec | RS.03.G |
| Exothermic peak at 130°C + 1% TBPB | 250 - 280 | °C | RS.03.G |
| Specific weight at 20°C | 1,11 | g/cm3 | — |
| Acidity at 130°C + 1% TBPB | 15 - 19,5 | mg KOH/g | MT-CU001I |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 3700 | MPa | ISO 527 (2012) |
| Flexural strength at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 100 | MPa | ISO 178/B (2010) |
| Flexural modulus at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 3700 | MPa | ISO 178/B (2010) |
| HDT at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 123 (145 *) | °C | ISO 75 -2A (2013) |
| Elongation at break at 70°C for 16h/ +2h at 100°C + 1h at 100°C | 1,5 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature