- Clear unaccelerated
- Type 1120 (DIN 16946-2)
- Type UP 0 (DIN 18820-1)
- Type UP 1A (EN 13121-1)
Applications & Uses
- Applications
- Composites Processing Methods
- Recommended Applications
Pipes and tanks
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1,10 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 2 rpm 100 | 185 - 225 | mPa.s | MT-CU023V |
| Solid Content | 53 - 58 | % | MT-CU001C |
| Peak at 20°C + 0,25% Co 4% + 2% MEKP50 | 15 - 30 | — | RS.03.G |
| Exothermic peak at 20°C + 0,25% Co 4% + 2% MEKP50 | 160 - 185 | °C | RS.03.G |
| Acidity at 20°C + 0,25% Co 4% + 2% MEKP50 | 11-17 | mg KOH/g | MT-CU001I |
| Value | Units | Test Method / Conditions | |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 100 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 43 | — | ASTM D 2583 (2007) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 74 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3450 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 87 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3,6 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature