Features & Benefits
- Materials Features
- Product Highlights
- Fire retardand properties
- Filled
- Very good glass wet-out
- Medium viscosity
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 700 - 900 | mPa.s | MT-CUT23V |
| Solid Content | 72 - 76 | % | MT-CU001C |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 12-16 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 33 - 43 | — | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 45 - 55 | °C | MT-CU152R |
| Specific weight at 20°C | 1,6 | g/cm3 | — |
| Value | Units | Test Method / Conditions | |
| Tensile strength at 40°C for 16h/+ 2 h at 90°C | 45 | MPa | ISO 527 (2012) |
| Tensile Modulus at 40°C for 16h/+ 2 h at 90°C | 3550 | MPa | ISO 527 (2012) |
| Flexural strength at 40°C for 16h/+ 2 h at 90°C | 90 | MPa | ISO 178 (2011) |
| Flexural modulus at 40°C for 16h/+ 2 h at 90°C | 3500 | MPa | ISO 178 (2011) |
| HDT at 40°C for 16h/+ 2 h at 120°C | 65 | °C | ISO 75 -2A (2013) |
| Elongation at break at 40°C for 16h/+ 2 h at 90°C | 1,55 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature