Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Form
- Reinforcement Material
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Compatible Reinforcements
- Composites Processing Methods
- Applications
espol™ 19.00 should be stored between 5°C and 25°C in the original, unopened container in a dry, well ventilated place. Protect from freezing and direct sunlight. Avoid contact with oxidizing agents. If stored outside of these recommendations, shelf life will be significantly reduced.
- Formulation Guidelines
- espol™ 19.00 should be allowed to attain workshop temperature (25°C - 30°C) before use. Stir well by hand, or with a low shear mixer to avoid aeration, and then allow to stand to regain thixotropy. espol™ 19.00 requires the addition of accelerator and catalyst to start the curing reaction.
- The recommended accelerator is Cobalt (1% solution in styrene) which should be added to the resin at 1 - 2% and thoroughly incorporated into the resin, using a low shear mechanical stirrer where possible.
- The recommended catalyst is AAP which should be added to the resin at 1 – 1.5% and thoroughly incorporated into the resin, using a low shear mechanical stirrer where possible.
N.B. Catalyst and accelerator must not be mixed directly together since they can react with explosive violence
Properties
- Color
- Appearance
- Light pale yellow clear liquid
- Cured Properties
- Uncured Properties
- Note
- *Curing Schedule - 24 hours at 20°C, 6 hours at 80°C.
- **100g resin + 2ml Co (1%) accelerator + 1.2ml AAP Catalyst.
- ***Viscosity measured using Brookfield (RVT Model) Viscosity SPL 1 / SPD 10
Value | Units | Test Method / Conditions | |
Barcol Hardness | 40 | — | IS 6746-1994 (Reaffirmed 2005) |
Deflection Temperature under Load (1.80MPa)* | 70 | ºC | IS 6746-1994 (Reaffirmed 2005) |
Tensile Strength* | 55 - 65 | MPa | IS 6746-1994 (Reaffirmed 2005) |
Tensile Modulus* | 3000 - 3300 | MPa | IS 6746-1994 (Reaffirmed 2005) |
Elongation at Break* | 1.5 - 2.5 | % | IS 6746-1994 (Reaffirmed 2005) |
Flexural Strength* | 90 - 100 | MPa | IS 6746-1994 (Reaffirmed 2005) |
Flexural Modulus* | 3000 - 3400 | MPa | IS 6746-1994 (Reaffirmed 2005) |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.06 - 1.1 | — | IS 6746-1994 (Reaffirmed 2005) |
Viscosity (at 25°C)* | 200 - 300 | cP | IS 6746-1994 (Reaffirmed 2005) |
Acid Value | 22 - 28 | mg KOH/g | IS 6746-1994 (Reaffirmed 2005) |
Volatile Content | 34 - 40 | % | IS 6746-1994 (Reaffirmed 2005) |
Gel Time (at 30°C)** | 9 - 15 | min | IS 6746-1994 (Reaffirmed 2005) |
Peak Exotherm Temperature** | 160 - 200 | ºC | IS 6746-1994 (Reaffirmed 2005) |
Technical Details & Test Data
- Post Curing
Satisfactory laminates for many applications can be made from espol™ 19.00 by curing at workshop temperature (25°C). For optimum properties, however, laminates should be post-cured before being put into service. The laminate should be allowed to cure for 24 hours at 25°C, and then be oven cured for a minimum of 6 hours 80°C.
Packaging & Availability
- Packaging Type
- Packaging Information
espol™ 19.00 is available in 35kg, 220kg and bulk containers.
Storage & Handling
- Shelf Life
- 3 Months
- Storage Conditions
espol™ 19.00 should be stored between 5°C and 25°C in the original, unopened container in a dry, well ventilated place. Protect from freezing and direct sunlight. Avoid contact with oxidising agents. If stored outside of these recommendations, shelf life will be significantly reduced.