| Value | Units | Test Method / Conditions | |
| Solid Content | 65 - 69 | % | MT-CU001C |
| Specific weight at 20°C | 1,39 | g/cm3 | — |
| Brookfield Viscosity at 23°C, sp 3 rpm 50 | 550 - 750 | mPa.s | MT-CU025V |
| Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 16 - 22 | minutes | MT-CU152R |
| Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 23 - 33 | minutes | MT-CU152R |
| Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 115 - 145 | °C | MT-CU152R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 80°C for 16h / +2h at 140°C | 0,72 | % | ISO 527 (2012) |
| Tensile strength at 80°C for 16h / +2h at 140°C | 25 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16h / +2h at 140°C | 3479 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 16h / +2h at 140°C | 60 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16h / +2h at 140°C | 3276 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16h / +2h at 140°C | 129 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature