Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Very long shelf life
- High reactivity
- Preaccelerated
Applications & Uses
- Applications
- Composites End Use
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Solid Content | 56 - 60 | % | MT-CU001C |
| Brookfield Viscosity at 23°C, sp 2 rpm 50 | 170 - 230 | mPa.s | MT-CU023V |
| Gel Time at 23°C + 2% PBO50 | 1:30 - 2:30 | minutes | MT-CU162R |
| Peak at 23°C + 2% PBO50 | 4:30 - 7:30 | minutes | MT-CU162R |
| Exothermic peak at 23°C + 2% PBO50 | 100 - 120 | °C | MT-CU162R |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 80°C for 16h / +2h at 120°C | 2,4 | % | ISO 527 (2012) |
| Curing Cycle at 80°C (120°C) | 16 (+2) | hr | — |
| Tensile strength at 80°C for 16h / +2h at 120°C | 65 | MPa | ISO 527 (2012) |
| Tensile Modulus at 80°C for 16h / +2h at 120°C | 3800 | MPa | ISO 527 (2012) |
| Flexural strength at 80°C for 16h / +2h at 120°C | 140 | MPa | ISO 178 (2011) |
| Flexural modulus at 80°C for 16h / +2h at 120°C | 4100 | MPa | ISO 178 (2011) |
| HDT at 80°C for 16h / +2h at 120°C | 90 | °C | ISO 75 -2A (2013) |
Storage & Handling
- Shelf Life
- 9 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature