Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Preaccelerated
- Reduced fiber print-through
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 400 - 500 | mPa.s | MT-CU025V |
| Solid Content | 55 - 62 | % | MT-CU001C |
| Gel Time at 25°C + 2% MEKP50 | 55 - 65 | minutes | RS.08.G |
| Curing Time at 25°C + 2% MEKP50 | 64 - 81 | minutes | RS.08.G |
| Exothermic peak at 25°C + 2% MEKP50 | 170 - 200 | °C | RS.08.G |
| Value | Units | Test Method / Conditions | |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 75 | °C | ISO 75 -2A (2013) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 40 | MPa | ISO 527 (2012) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2,7 | % | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2400 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 70 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 2300 | MPa | ISO 178/B (2010) |
| Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 109 | °C | ASTM E 1545 (2011) |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 28 | — | ASTM D 2583 (2007) |
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature