Glass-fiber reinforced Polyester molding compound
Low mold shrinkage and post-shrinkage, good electrical values, good heat resistance, good mechanical strength
Primary application(s): molded parts in electrical engineering
This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)
Identification according to ISO 14530-3:UP (GF10 + MD65) - (GF20 + MD55)DIN 7708: UP 804
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Supply form
Low dust granulate in moisture resistant bags
- Processing
- Injection and compression molding
Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Compressive strength | 150 - 200 | MPa | ISO 604 |
E-Modulus (flexural test) | 8 - 12 | GPa | ISO 178 |
E-Modulus (tensile test) | 6 - 9 | GPa | ISO 527 |
Flexural strength | 100 - 120 | MPa | ISO 178 |
Impact strength (Charpy) | 8 - 11 | kJ/m² | ISO 179 / 1eU |
Impact strength (Charpy), notched | 3,0 - 4,0 | kJ/m² | ISO 179 / 1eA |
Tensile strength | 40 - 70 | MPa | ISO 527 |
Value | Units | Test Method / Conditions | |
Coeff. of linear thermal expansion (longitudinal,50-100°C) | 10 - 20 | 10-6 / K | ISO 11359-2 |
Maximum application temperature (20 000 h) | 180 | °C | IEC 60216/T1 |
Flammability | V-0 / 3,0 | Stufe/mm | UL 94 |
Thermal conductivity | 0,9 - 1,1 | W / m * K | ASTM E 1461 |
Glow wire flammability test / GWFI | 960 / 1 | — | IEC60695-2-12 |
Glow wire ignitability test / GWIT | 930 / 1 | — | IEC60695 2-13 |
Heat deflection temp. HDT A - 1,80 MPa | min. 175 | °C | ISO 75 |
Heat deflection temp. HDT C - 8,00 MPa | 125 - 150 | °C | ISO 75 |
Maximum application temperature (<50 h) | 210 | °C | IEC 60216/T1 |
Value | Units | Test Method / Conditions | |
Moulding shrinkage (longitudinal) | 0,2 - 0,5 | % | ISO 2577 |
Moulding shrinkage (longitudinal) | 0,2 - 0,5 | % | ISO 2577 |
Post shrinkage (168 h / 110 °C) | max. 0,1 | % | ISO 2577 |
Post shrinkage (168 h / 110 °C) | max. 0,1 | % | ISO 2577 |
Specific gravity | 1.90 - 2.10 | g/cm³ | ISO 1183 |
Water absorption (24 h / 23 °C) | max. 35 / max. 0,5 | mg / % | ISO 62 |
Apparent Density | 0.75 - 1.00 | g/cm³ | ISO 60 |
Value | Units | Test Method / Conditions | |
Dissipation factor (100 Hz/1 MHz) | 0,01-0,03 / 0,01-0,03 | — | IEC 60250 |
Relative permittivity (100 Hz/1 MHz) | 5 - 6 / 4 - 5 | — | IEC 60250 |
Surface resistance | 10^12 - 10^13 | Ω | IEC 60093 |
Tracking resistance (CTI) | 600 | V | IEC 60112 |
Volume resistivity | 10^13 - 10^14 | Ω cm | IEC 60093 |
Arc resistance | 4 | Stufe | ASTM D 495 |
Dielectric strength | 25 - 35 | kV / mm | IEC 60243-1 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Type
Storage & Handling
- Storage conditions / shelf life
Keep cool and dry.Minimum shelf life at 20 ± 5 °C:6 months after date of delivery