LNP™ COLORCOMP™ Compound E1000CE

Identification & Functionality

Additives Included

UV Stabilizer

Chemical Family

Polyetherimide (PEI),

Polyimides (PI)

Polymer Name

Polyether Imide (PEI)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Easy To Mold,

Excellent Aesthetics,

Good Aesthetics,

Good Moldability,

Good Processability,

Good Surface Appearance,

Good UV Stability,

Good Weather Stability,

High Durability,

High Temperature Resistance,

Low Liquid Particle Count,

Low Outgassing,

UV Resistant,

UV Stabilized,

Unreinforced,

Very Good Heat Resistance

Product Features

• VR: 10'7
• FM: 3.51GPa
• Low ionic
• FM4910 compliant

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Cell Phones,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Industrial Applications,

Semiconductor Applications,

Tablets,

Trays

Plastics & Elastomers Processing Methods

Injection Molding

Possible Applications

• FOUP housing
• SMIF POD housing

Properties

Color

Custom

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	110	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	60	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	3580	MPa	ASTM D638
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	165	MPa	ASTM D790
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	3510	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	109	—	ASTM D785
Taber Abrasion (CS-17, 1 kg) ¹¹	10	mg/1000cy	ASTM D1044

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.27	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.25	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	1.25	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 337°C, 6.6 kgf) ¹¹	17.8	g/10 min	ASTM D1238

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate B/50) ¹¹	218	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	207	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	198	°C	ASTM D648
Coefficient of Thermal Expansion (at -20°C to 150°C, flow) ¹¹	0.0000558	1/°C	ASTM E831
Thermal Conductivity ¹¹	0.22	W/m-°C	ASTM C177

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	1.00E+17	Ω.cm	ASTM D257
Dielectric Strength (in air, at 1.6mm) ¹¹	32.6	kV/mm	ASTM D149
Dielectric Strength (in oil, at 1.6mm) ¹¹	27.9	kV/mm	ASTM D149
Relative Permittivity (1 kHz) ¹¹	3.15	—	ASTM D150
Dissipation Factor (at at 1 kHz) ¹¹	0.0013	—	ASTM D150
Dissipation Factor (at 2450 MHz) ¹¹	0.0025	—	ASTM D150

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1335	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	32	J/m	ASTM D256
Izod Impact (Reverse Notched, 3.2 mm) ¹¹	1174	J/m	ASTM D256
Color (at 23°C) ¹¹	3.30E+01	J	ASTM D3029

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	360 - 400	°C	—
Rear - Zone 1 Temperature ⁷	360 - 380	°C	—
Middle - Zone 2 Temperature ⁷	370 - 390	°C	—
Front - Zone 3 Temperature ⁷	380 - 400	°C	—
Nozzle Temperature ⁷	390 - 400	°C	—
Mold Temperature ⁷	140 - 180	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed (Circumferential speed) ⁷	0.2 - 0.3	m/s	—
Vent Depth ⁷	0.025 - 0.076	mm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
Oxygen Index (LOI)	44	%	ASTM D2863
NBS Smoke Density (Flaming, Ds 4 min)	2	—	ASTM E662

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 