LNP™ LUBRICOMP™ Compound DX94375H

Identification & Functionality

Chemical Family

Polycarbonate (PC)

Fillers Included

PTFE,

Silicone Oil

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Materials Features

Friction Resistant,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Oil/Gas Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	52	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	49	MPa	ISO 527
Tensile Stress (Break) ¹¹	44	MPa	ASTM D638
Tensile Stress (Break) ¹¹	43	MPa	ISO 527
Tensile Strain (Yield) ¹¹	5.7	%	ASTM D638
Tensile Strain (Yield) ¹¹	5.1	%	ISO 527
Tensile Strain (Break) ¹¹	56	%	ASTM D638
Tensile Strain (Break) ¹¹	52	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	1860	MPa	ASTM D638
Flexural Stress ¹¹	81	MPa	ISO 178
Flexural Stress ¹¹	68	MPa	ASTM D790
Flexural Modulus ¹¹	2300	MPa	ISO 178
Flexural Modulus ¹¹	2040	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	2100	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.27	g/cm³	ISO 1183
Density ¹¹	1.27	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.9 - 1.1	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.9 - 1.1	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 1.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 1.2	%	ISO 294

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	128	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	149	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	33	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	137	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	19	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	300 - 315	°C	—
Front - Zone 3 Temperature ⁷	310 - 320	°C	—
Middle - Zone 2 Temperature ⁷	305 - 315	°C	—
Rear - Zone 1 Temperature ⁷	295 - 305	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 