LNP™ LUBRILOY™ Compound RF203XXH

Identification & Functionality

Additives Included

Lubricant (Unspecified),

Proprietary

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Lubricated,

Wear Resistant

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Electronic Components,

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	87	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3.7	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	4890	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	128	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	4180	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.8	%	ISO 527
Flexural Stress ¹¹	140	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5500	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.12	—	ASTM D792
Density ¹¹	1.13	g/cm³	ASTM D792
Density ¹¹	1.13	g/cm³	ISO 1183
Wear Factor Washer ¹¹	70	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.36	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.3	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ⁷	232	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	646	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	83	J/m	ASTM D256
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	9	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	270 - 280	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 