LNP STAT-KON™ Compound - 5E003M - SABIC's Specialty

Identification & Functionality

Chemical Family: Vinyls, Vinylics & Vinyl Derivatives
Fillers Included: Carbon Fiber,
Milled Carbon Fiber
Polymer Name: Polyvinylidene Fluoride (PVDF)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Dimensional Stability,
Electrically Conductive,
High Stiffness,
Light Weight

Applications & Uses

Markets: Electrical & Electronics,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Industrial Automation
Electrical & Electronics — Parts & Components
Semiconductor Manufacturing
Industrial — Power, Water & Utilities
Renewable Energy
Plastics & Elastomers End Uses: Electrical/Electronic Applications,
Energy Management,
Industrial Applications,
Semiconductor Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	50	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	47	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	3.5	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	6.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	9060	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	79	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	5470	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	49	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	46	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	3.4	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	6.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	7450	MPa	ISO 527
Flexural Stress ¹¹	79	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6580	MPa	ISO 178

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.76	—	ASTM D792
Density ¹¹	1.76	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.04	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	5.00E-02	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	160	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	136	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.00002	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000092	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	150	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	114	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	432	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	58	J/m	ASTM D256
Multi-Axial Impact ¹¹	3	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	13	J	ASTM D3763
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	26	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ STAT-KON™ Compound 5E003M