LNP™ STAT-LOY™ Compound M3000C

Identification & Functionality

Additives Included

Anti-Static Agent,

Heat Stabilizer,

Impact Modifier

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Proprietary

Polymer Name

Polypropylene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Anti-Static,

Heat Stabilized,

Impact Modified,

Low Liquid Particle Count,

Low Outgassing,

No Added PFAS,

Unreinforced

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Cell Phones,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	689	%	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	18	MPa	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	760	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	24	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	860	MPa	ASTM D790
Tensile Stress (Break, 50 mm/min) ¹¹	24	MPa	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	690	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1180	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	38	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	1960	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	0.93	g/cm³	ASTM D792
Density ¹¹	0.93	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.16	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1 - 2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 2	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.16	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	74	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	49	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000128	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000131	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	75	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	49	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ᵈ ¹¹	10000000000 - 1000000000000	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	75	J/m	ASTM D256
Multi-Axial Impact ¹¹	25	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	29	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	70 - 80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	190 - 200	°C	—
Front - Zone 3 Temperature ⁷	200 - 210	°C	—
Middle - Zone 2 Temperature ⁷	195 - 205	°C	—
Rear - Zone 1 Temperature ⁷	180 - 195	°C	—
Mold Temperature ⁷	30 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵈ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding. Do NOT mix NORYL GTX* resin with other grades of NORYL* resins. Polystyrene and acrylic regrind are effective purging Materials. Use temperature range appropriate for particular purging resin. Regrind must also be dried. Maximum 25% regrind. Dry at recommended temperatures and times for optimum performance. Overdrying can cause loss of physical properties and/or create appearance defects. Do not exceed recommended basic drying time and temperature above or:\n4-8 hrs at 95°C (200°F), 10 hrs max\n6-12 hrs at 80°C (175°F), 16 hrs max\n8-16 hrs at 65°C (150°F), 24 hrs max\nAVOID air circulating tray ovens. Moisture levels in heated ambient air can exceed moisture level in the resin itself, causing moisture ABSORPTION not drying. Avoid melt temperature in excess of 300°C (575°F) and residence times over 6-8 minutes (may affect properties and/or appearance). Nozzle temperature controls assist in elimination of drool premature freeze-off. Shot sizes in excess of 50% barrel capacity can lead to difficulties in providing a consistent, homogenous plastic melt.
• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 