LNP THERMOCOMP™ Compound - 2Z004 - SABIC's Specialty

Identification & Functionality

Chemical Family: Fluoropolymers,
Polyolefins
Fillers Included: Glass Fiber,
Milled Glass Fiber
Polymer Name: Ethylene Tetrafluoroethylene Copolymer (ETFE)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Cost Effective,
Dimensional Stability,
High Impact Resistance,
Low Warpage

Applications & Uses

Markets: Electrical & Electronics,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Industrial Automation
Electrical & Electronics — Parts & Components
Housings & Enclosures,
Semiconductor Manufacturing
Industrial — Power, Water & Utilities
Renewable Energy
Plastics & Elastomers End Uses: Electrical/Electronic Applications,
Enclosure,
Energy Management,
Industrial Applications,
Semiconductor Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Physical Properties
Mechanical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.84	—	ASTM D792
Density ¹¹	1.83	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.01	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1 - 2	%	ASTM D955

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	29	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	21	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	23	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	53	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	1700	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	1280	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	27	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	22	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	22	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	78	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1510	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	24	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	1210	MPa	ISO 178

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	88	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	52	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.00008	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000087	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	89	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	50	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1340	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	615	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	26	J	ASTM D3763
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	119	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	37	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ THERMOCOMP™ Compound 2Z004