LNP™ THERMOCOMP™ Compound OF008H

Identification & Functionality

Chemical Family

Polyphenylene Sulfide (PPS)

Fillers Included

Glass Fiber

Polymer Name

Polyphenylene Sulfide (PPS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

High Impact Resistance,

High Linearity,

High Modulus,

High Stiffness,

No Added PFAS

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	140	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.6	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	14100	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	234	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	14220	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.7	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1	%	ASTM D955
Wear Factor Washer ¹¹	373	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.41	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.5	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	264	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	534	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	96	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	315 - 320	°C	—
Front - Zone 3 Temperature ⁷	330 - 345	°C	—
Middle - Zone 2 Temperature ⁷	320 - 330	°C	—
Rear - Zone 1 Temperature ⁷	305 - 315	°C	—
Mold Temperature ⁷	140 - 165	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Compliant (94V-0 Flame Class Rating)	0.45	mm	UL 94 by SABIC-IP

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA