LNP THERMOCOMP RF006H compound is based on Nylon 6/6 resin containing 30% glass fiber. Added features of this grade include: Healthcare.

Polymer Name: Polyamide 66 (PA 66)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber

Flexural Modulus: 9220.0 - 9220.0 MPa

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Cost Effective,

High Stiffness

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Healthcare Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Physical Properties
ValueUnitsTest Method / Conditions
Density⁴⁹0.000105g/cm³ASTM D792 (ISO 1183)
Mold Shrinkage - flow (24 hrs)¹²,⁴⁹0.3 - 0.5%ASTM D955 (ISO 294)
Mold Shrinkage - xflow (24 hrs)¹²,⁴⁹0.000105%ASTM D955 (ISO 294)
Dynamic COF⁴⁹0.71-ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C / 50% RH)⁴⁹1.2%ISO 62
Moisture Absorption (at 23°C/50% RH/24 hrs)⁴⁹0.69%ASTM D570
Specific Gravity⁴⁹1.41-ASTM D792
Static COF⁴⁹0.57-ASTM D3702 Modified: Manual
Wear Factor Washer⁴⁹7510^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Mechanical Properties
ValueUnitsTest Method / Conditions
Flexural Modulus (1.3 mm/min, 50 mm span)⁴⁹9440MPaASTM D790
Flexural Modulus (2 mm/min)⁴⁹9220MPaISO 178
Flexural Stress at Break (1.3 mm/min, 50 mm span)⁴⁹235MPaASTM D790
Tensile Modulus (1 mm/min)⁴⁹8980MPaISO 527
Tensile Strain at Break (5 mm/min)⁴⁹2.4%ISO 527
Tensile Strain at Break (Type I, 5 mm/min)⁴⁹2.4%ASTM D638
Tensile Stress at Break (5 mm/min)⁴⁹154MPaISO 527
Tensile Stress at Break (Type I, 5 mm/min)⁴⁹165MPaASTM D638
Thermal Properties
ValueUnitsTest Method / Conditions
CTE - flow (at -40°C to 40°C)⁴⁹0.0001051/°CASTM E831 (ISO 11359-2)
CTE - xflow (at -40°C to 40°C)⁴⁹0.0001051/°CASTM E831 (ISO 11359-2)
HDT - Unannealed (0.45 MPa, 3.2 mm)⁴⁹265°CASTM D648
HDT - Unannealed (1.82 MPa, 3.2mm)⁴⁹255°CASTM D648
HDT/Af (1.8 MPa Flatw 80*10*4 sp=64mm)⁴⁹243°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Instrumented Dart Impact Energy at Peak (at 23°C)⁴⁹6JASTM D3763
Izod Impact Notched (80*10*4 +23°C)⁴⁹7kJ/m²ISO 180/1A
Izod Impact Notched (at 23°C)⁴⁹58J/mASTM D256
Izod Impact Unnotched (80*10*4 +23°C)⁴⁹52kJ/m²ISO 180/1U
Izod Impact Unnotched (at 23°C)⁴⁹646J/mASTM D4812
Multiaxial Impact⁴⁹2JISO 6603
Injection Molding
ValueUnitsTest Method / Conditions
Back Pressure⁴²0.2 - 0.3MPa-
Drying Temperature⁴²80°C-
Drying Time⁴²4Hrs-
Front - Zone 3 Temperature⁴²295 - 305°C-
Maximum Moisture Content⁴²0.15 - 0.25%-
Melt Temperature⁴²280 - 305°C-
Middle - Zone 2 Temperature⁴²280 - 295°C-
Mold Temperature⁴²95 - 110°C-
Rear - Zone 1 Temperature⁴²265 - 275°C-
Screw Speed⁴²30 - 60rpm-
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Compliant 94HB Flame Class Rating²⁷1.5mmUL 94 by SABIC-IP
Note
  • ⁴² Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ²⁷ UL rating shown here is based on internal measurements.
  • ⁴⁹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
  • ¹² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability
  • Asia
  • Europe
  • North America