LNP™ THERMOCOMP™ Compound RX10405H

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Carbon Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

Electrically Conductive,

High Stiffness,

High Strength,

Light Weight,

No Added PFAS

Applications & Uses

Markets

Healthcare & Pharma,

Printing & Packaging

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies,

Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging,

Industrial & Transport Packaging

Plastics & Elastomers End Uses

Medical Devices,

Medical Packaging,

Medical/Healthcare Applications,

Pharmaceutical Packaging,

Surgical Devices

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	276	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.6	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	31000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	386	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	24400	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.33	—	ASTM D792

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	256	°C	ASTM D648

Electrical Properties

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	100	Ω	ASTM D257

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	101	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	280 - 305	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	95 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America