LNP™ THERMOTUF™ Compound IX02582

Identification & Functionality

Additives Included

Heat Stabilizer,

Impact Modifier

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

Proprietary

Polymer Name

Polyamide 612 (PA 612)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Heat Stabilized,

High Impact Resistance,

High Modulus,

High Stiffness,

Impact Modified,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Industrial — Military & Defense

Advanced Materials

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Food Preparation Equipment,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Military Applications,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	156	MPa	ASTM D638
Tensile Stress (Break) ¹¹	174	MPa	ASTM D638
Flexural Modulus ¹¹	10340	MPa	ASTM D790
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.8	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	12120	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	233	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	235	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	9700	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	157	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11810	MPa	ISO 527
Flexural Stress ¹¹	233	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	9980	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.41	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.25	%	ASTM D570
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.16	%	ASTM D570
Specific Gravity ¹¹	1.41	—	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.1 - 0.3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.28	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	214	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	198	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000039	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000075	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	210	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	196	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	158	J/m	ASTM D256
Izod Impact (Notched, at 23°C) ¹¹	208	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	995	J/m	ASTM D4812
Multi-Axial Impact ¹¹	5	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	20	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	62	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	15	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.12 - 0.2	%	—
Melt Temperature ⁷	270 - 275	°C	—
Front - Zone 3 Temperature ⁷	270 - 280	°C	—
Middle - Zone 2 Temperature ⁷	260 - 270	°C	—
Rear - Zone 1 Temperature ⁷	255 - 265	°C	—
Mold Temperature ⁷	65 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 