NORYL™ Resin GFN2F

Identification & Functionality

Additives Included

Mold Release Agent

Fillers Included

Glass Fiber

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Food Contact Acceptable,

No Added PFAS

Materials Features

Amorphous,

Dimensional Stability,

Excellent Stiffness,

Food Contact Acceptable,

Good Mold Release,

Good Stiffness,

High Hydrolytic Stability,

High Stiffness,

Low Corrosion,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Industrial

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Power, Water & Utilities

Water Treatment

Plastics & Elastomers End Uses

Faucet System Components,

Filters,

Fittings,

Gears,

Hygiene,

Potable Water Applications,

Pump Parts,

Water Management

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	90	MPa	ASTM D638
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	100	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2.6	%	ASTM D638
Tensile Stress (Yield, Type I, 10 mm/min) ¹¹	88	MPa	SABIC - Japan Method
Tensile Modulus (at 5 mm/min) ¹¹	6200	MPa	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	6500	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	160	MPa	ASTM D790
Tensile Strain (Yield, Type I, 10 mm/min) ¹¹	6 - 8	%	SABIC - Japan Method
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	5800	MPa	ASTM D790
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	131	MPa	ASTM D790
Hardness (Rockwell L) ¹¹	106	—	ASTM D785
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	5570	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	97	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3	%	ISO 527
Tensile Stress (Yield, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6000	MPa	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	7070	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	150	MPa	ISO 178
Flexural Stress (Yield, at 2 mm/min) ¹¹	167	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5400	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6540	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.2	—	ASTM D792
Specific Gravity ¹¹	1.23	—	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.12	%	ISO 62-1
Water Absorption (at 23°C, 24hrs) ¹¹	0.06	%	ASTM D570
Mold Shrinkage (flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹	9	g/10 min	ASTM D1238
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹	11.7	g/10 min	ASTM D1238
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.04	%	ISO 62
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹	2	cm³/10 min	ISO 1133
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.2 - 0.5	%	SABIC method
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	8	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	140	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	135	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	143	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	138	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹	0.000028 - 0.000045	1/°C	TMA
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000289	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000826	1/°C	ASTM E831
Vicat Softening Temperature (Rate B/50) ¹¹	143	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	140	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	146	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	147	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	135	°C	ISO 75/Af
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	143	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	137	°C	ISO 75/Ae
Relative Temperature Index (Electrical) ᵖ ¹¹	90	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	90	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	90	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index (UL, PLC) ¹¹	4	PLC Code	UL 746A
High Ampere Arc Ignition (PLC 4) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 6	mm	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 3	mm	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	4	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	6	PLC Code	ASTM D495
Arc Resistance (Tungsten, PLC) ¹¹	7	PLC Code	ASTM D495
Dielectric Strength (in oil, at 3.2mm) ¹¹	16.5	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	2.86	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0008	—	ASTM D150
High Ampere Arc Ignition (PLC 3) ¹¹	min. 6	mm	UL 746A
Hot Wire Ignition (PLC 4) ¹¹	min. 1.5	mm	UL 746A

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	550	J/m	ASTM D4812
Izod Impact (Unnotched, at 23°C) ¹¹	650	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	88	J/m	ASTM D256
Izod Impact (Notched, at 23°C) ¹¹	119	J/m	ASTM D256
Izod Impact (Notched, at -40°C) ¹¹	96	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	20	J	ASTM D3763
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	22	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	11	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Charpy Impact (Notched, at 23°C) ¹¹	11	kJ/m²	ISO 179/2C
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	9	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	8	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	110 - 120	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	300 - 325	°C	—
Nozzle Temperature ⁷	300 - 325	°C	—
Front - Zone 3 Temperature ⁷	290 - 325	°C	—
Middle - Zone 2 Temperature ⁷	275 - 320	°C	—
Rear - Zone 1 Temperature ⁷	265 - 315	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ʳ	min. 1.5	mm	UL 94
UV-light (Water exposure/immersion) ʳ	F1	—	UL 746C
Oxygen Index (LOI) ʳ	26	%	ASTM D2863

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

NSF Standard 61 for Drinking Water,

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• Global
• North America