Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 35 | MPa | ISO 527 |
Tensile Stress (Yield) ¹¹ | 35 | MPa | SABIC - Japan Method |
Tensile Strain (Break) ¹¹ | 150 | % | SABIC - Japan Method |
Tensile Stress (Break, 50 mm/min) ¹¹ | 35 | MPa | ISO 527 |
Flexural Stress ¹¹ | 55 | MPa | ASTM D790 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 3 | % | ISO 527 |
Flexural Modulus ¹¹ | 1740 | MPa | ASTM D790 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 70 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 1750 | MPa | ISO 527 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 55 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 1800 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.06 | — | ASTM D792 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.8 | % | SABIC method |
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹ | 14 | g/10 min | ASTM D1238 |
Density ¹¹ | 1.08 | g/cm³ | ISO 1183 |
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 6 | cm³/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 105 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.00007 | 1/°C | TMA |
Ball Pressure Test (at 73°C to 77°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 110 | °C | ISO 306 |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 105 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 95 | °C | ISO 75/Af |
Value | Units | Test Method / Conditions | |
Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 2.74E+02 | J/m | ASTM D256 |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 21 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 16 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 - 100 | °C | — |
Drying Time ⁷ | 2 - 4 | Hrs | — |
Melt Temperature ⁷ | 280 - 300 | °C | — |
Nozzle Temperature ⁷ | 260 - 280 | °C | — |
Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C | — |
Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C | — |
Hopper Temperature ⁷ | 60 - 80 | °C | — |
Mold Temperature ⁷ | 60 - 100 | °C | — |